For more information, contact Joel W. Sills, Langley Research Center, [email protected]. Download PDF here Chip resistors are widely used in NASA projects, yet cases of alumina substrate cracking during environmental testing are rare. Two instances of thick-film chip resistor cracking were observed during thermal cycling after vibration, with fractures occurring across the short axis due []
TB 26-10 Printed Circuit Board Assembly Chip Resistor Body Cracking
NASA Breaking news - 3 Nov 2026 15:35
For more information, contact Joel W. Sills, Langley Research Center, [email protected]. Download PDF here Chip resistors are widely used in NASA projects, yet cases of alumina substrate cracking during environmental testing are rare. Two instances of thick-film chip resistor cracking were observed during thermal cycling after vibration, with fractures occurring across the short axis due []